NO. | TEST ITEM | TEST CONDITION | DURATION | REFERENCE DOCUMENT |
1 | SOLDERABILITY | 230°C ~ 260°C | 5SEC 1 TIME | MIL-STD-750B METHOD 2062.3 |
2 | LEAD TENSION | 2KG IN LEAD DIRECTION | 10SEC | MIL-STD-750B METHOD 2036.3 |
3 | LEAD FATIGUE | 90°C BEND WITH 0.5KG WEIGHT ATTACHED TO LEAD |
3 TIMES | MIL-STD-750B METHOD 2036.3 |
4 | LEAD TORQUE | 1.45+-0.145KG-MM | 1 TIME | MIL-STD-750B METHOD 2036.3 |
5 | OPERATING LIFE | RATED VOLTAGE & CURRENT @25°C |
168/1000HRS | MIL-STD-750B METHOD 1027.1 |
6 | HIGH TEMPERATURE REVERSE BIAS |
80% RATED VOLTAGE@150°C | 168/1000HRS | MIL-STD-750B METHOD 1039 |
7 | INTERMITTENT OPERATING LIFE |
ON-WITH RATED IC,IB OFF-WITH COOL FORCE FAN Tc=60 - 70°C |
1000CYCLES | MIL-STD-750B METHOD 1036.3 |
8 | HIGH TEMPERATURE STORAGE LIFE |
@150°C | 168/1000HRS | MIL-STD-750B METHOD 1031.4 |
9 | MOISTURE RESISTANCE |
85°C/85%RH | 168/1000HRS | MIL-STD-750B METHOD 1021.1 |
10 | PRESSURE COOK | 119.6°C/2ATM | 48/144HRS | MIL-S-19500 APPENDIX C |
11 | THERMAL SHOCK | -40°c/5MIN ~ 150°C/5MIN 250C/10SEC FOR TRANSFER |
50/100CYCLES | MIL-STD-750B METHOD 1056.1 |
12 | TEMPERATURE CYCLING |
-65°C/30MIN ~ 150°C/30MIN 25°C/10MIN FOR TRANSFER |
50/100CYCLES | MIL-STD-750B METHOD 1051.2 |
13 | SOLDERING HEAT | 260°C +-5°C | 10SEC 1TIME | MIL-STD-750B METHOD 2031.1 |
14 | SALT SPRAY | 5% SALT SOLUTION UNDER 35°C AIR/47°C CHAMBER |
48HRS | MIL-STD-750B METHOD 1046.2 |